DOI10.1007/BF01215425zbMath0849.73053MaRDI QIDQ1914957

Brock, L. M.

Publication date: 19 November 1996

Published in: Acta Mechanica (Search for Journal in Brave)

zbMATH Keywords

tensionexact solutionsfully-plastic crack edge zonesmixed boundary/initial value problemsmultiple transform spaceSV-wave diffraction

Mathematics Subject Classification ID

Fracture and damage (74R99) Wave scattering in solid mechanics (74J20)

Related Items (1)

Slip/diffusion zone effects at rapidly-loaded cracks in thermoelastic solids

Cites Work

• Unnamed Item
• Unnamed Item
• Unnamed Item
• Unnamed Item
• Unnamed Item
• Unnamed Item
• Transient analyses of dislocation emission in the three modes of fracture
• An exact transient analysis of dislocation emission and fracture
• Transient studies of screw and edge dislocation generation at crack edges
• Thermal effects in rudimentary crack edge inelastic zone growth under stress wave loading
• Early transient response during crack propagation in a weakly-coupled thermoelastic solid
• A modification of cagniard’s method for solving seismic pulse problems
• Incident Wave and Dislocation Acceleration Effects in Dislocation Emission From Cracks
• Transient Coupled Thermoelastic Boundary Value Problems in the Half-Space

This page was built for publication: Transient thermal response near dynamically-loaded cracks during dislocation generation