Mixed mode failure criteria for brittle elastic V-notched structures

DOI10.1007/S10704-007-9098-XzbMath1198.76139OpenAlexW2032095117MaRDI QIDQ604289

Zohar Yosibash, Arie Bussiba, Ilan Gilad, Elad Priel

Publication date: 10 November 2010

Published in: International Journal of Fracture (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1007/s10704-007-9098-x

zbMATH Keywords

ceramicsV-notchfailure initiationmixed-modegeneralized stress intensity factorsp-version FEA

Mathematics Subject Classification ID

Stress concentrations, singularities in solid mechanics (74G70) Free convection (76R10)

Related Items (8)

\(T\)-stress effects on crack deflection: straight vs. curved crack advance ⋮ A 3-D failure initiation criterion from a sharp V-notch edge in elastic brittle structures ⋮ Two-dimensional fracture mechanics problems for solids with sharp and rounded V-notches ⋮ Computation of V-notch shape factors in four-point bend specimen for fracture tests on brittle materials ⋮ Generalised stress intensity factors for rounded notches in plates under in-plane shear loading ⋮ Fracture assessment of U-notches under mixed mode loading: two procedures based on the `equivalent local mode I' concept ⋮ Failure initiation at a blunt V-notch tip under mixed mode loading ⋮ Determination of mode II fracture toughness for U-shaped notches using Brazilian disc specimen

Cites Work

• A failure criterion for brittle elastic materials under mixed-mode loading
• Failure criteria for brittle elastic materials
• Fracture initiation at sharp notches: Correlation using critical stress intensities
• Strength or toughness? A criterion for crack onset at a notch

This page was built for publication: Mixed mode failure criteria for brittle elastic V-notched structures