Initial fracture process zone at the corner point of the interface between elastic bodies

DOI10.1007/s10778-012-0546-6zbMath1295.74091OpenAlexW2014262779MaRDI QIDQ741080

T. V. Polishchuk, Anatoly A. Kaminsky, Leonid A. Kipnis

Publication date: 10 September 2014

Published in: International Applied Mechanics (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1007/s10778-012-0546-6

zbMATH Keywords

interfaceWiener-Hopf methodfracture process zonecorner pointlines of discontinuity of normal displacement

Mathematics Subject Classification ID

Brittle fracture (74R10) Inhomogeneity in solid mechanics (74E05)

Related Items

Stress distribution around cracks in linear hardening materials subject to tension: Plane problem

Cites Work

• Unnamed Item
• Unnamed Item
• Unnamed Item
• Unnamed Item
• Unnamed Item
• On stability of the equilibrium of a Cottrell crack
• Fracture of a material compressed along a crack located at a short distance from the free surface
• Modeling the fracture process zone near a crack tip in a nonlinear elastic body
• Plastic rupture lines at the tip of a crack
• Some consequences of the inequality conditions in contact and crack problems
• Crack kinking from an interface crack with initial contact between the crack lips
• Slip-band propagation at the tip of an edge crack during plane deformation
• Initial Development of the Prefracture Zone Near the Tip of a Crack Reaching the Interface Between Dissimilar Media
• Analyzing the Laws of Stable Subcritical Growth of Cracks in Polymeric Materials on the Basis of Fracture Mesomechanics Models. Theory and Experiment